Synthene PRC1719 POLYOL

Any need for technical parts requiring quality of transparency, UV resistance and/or high mechanical properties, such as: Household appliances, electronics, toys, automotive industry: head lamps, head light, transparent pieces, crystal ware industries, glass making, bottles, advertising goods, design objects...
PRC 1719 POLYOL : Color: transparent / Viscosity : approximately450 mPa.s. Mix PRC 1719 POLYOL 0,6 Kg plus PRC 17XX ISO 1 Kg (ratio 60/100): Color: transparent / Viscosité : approximately400 mPa.s / PotLife : 19 min / Démoulding time at 70°C : 150 min / Simulation of: PMMA ou PC / HdT: 93°C / Hardness: 85 ShD / Flexural modulus of elasticity: 2200 Mpa / Refraction index at 20°C: 1,51 (ISO179-1/1eUꚝ:2010) / Hazen Coloration on 50mm : <30 / Charpy impact strength (ISO 179-1/1fUc: 2010) : 48kJ/m².
Transparent polyurethane resin dedicated to the production of prototypes and/or limited series. Process in vacuum casting machines with silicone moulds. Its properties allow the realisation of functional pieces: mechanical properties being simi-lar to transparent thermoplastic material such as PMMA or Polycarbonate.
Dangereux. Respecter les précautions d'emplois
See the different packaging


This product is not available online.Contact us
Name Code article Price Availability Security form
Synthene PRC1719 POLYOL
0,6 kg Bottle
SY5651 Contact us DownloadDownload the technical datasheet
Synthene PRC1719 POLYOL
3 kg Can
SY5652 Contact us DownloadDownload the technical datasheet


Application Methode Vacuum Casting
Curing Type Hot Curing
Density 1.1 kg_m3
Chemistry / Technology Polyurethane
Color Clear
Hardness Class Very Hard (Shore D56 - D100)
Hardness 84 Dshore
HDT - Heat Distorsion temperature 86 CELSIUS
Elongation at break (%) 15.0000
Flexural Modulus 2100 MegaPa
Multi parts product type Polyol
100 ml Pot-Life 19 MINUTE
100 ml Pot-Life 19 MINUTE
Number of Component Bi Componant / 2 Parts
Dynamic Viscosity (25°C) 450 mPas